Effect of Different Tempering Temperature and Different Load on Wear Behaviour and Mechanical Properties on Mild Steel

Authors

  • Amarishkumar J. Patel Mechanical Engineering Department, B&B Institute of technology V.v.nagar
  • Sunilkumar N. Chaudhari Mechanical Engineering Department, B&B Institute of technology V.v.nagar

Keywords:

Carburizing, Tempering, load, Wear test, Hardness test, tensile test, toughness test , carburizing time

Abstract

Heat treatment is process to modify the mechanical, physical and somewhat chemical properties by heating
or cooling at desired temperature. Carbon is absorbed in steel with help of coal material according to proper heating
and tempering time and temperature in carburizing process. The mild steel specimens are made from standard sample
size according to perform different test. The mild steel samples are carburized at 9000C temperature and socking time up
to 120 min. Then quenching in oil bath and tempered at different temperature like 2000C, 2500C, 3000C for ninety
minutes .These standard specimens perform under different test like 50N, 150N, and 250N load for wear test. Mechanical
test performed on their standard dimension and size according to hardness, tensile and toughness test. During this test
carburizing process improve the wear, hardness, tensile strength value and compromise in toughness at higher
tempering process in mild steel material.

Downloads

Published

2015-10-25

How to Cite

Amarishkumar J. Patel, & Sunilkumar N. Chaudhari. (2015). Effect of Different Tempering Temperature and Different Load on Wear Behaviour and Mechanical Properties on Mild Steel. International Journal of Advance Engineering and Research Development (IJAERD), 2(10), 69–76. Retrieved from https://ijaerd.org/index.php/IJAERD/article/view/4854